The Legor SCS3 league is an alloy for silver jewelry, which allows to obtain an antioxidant 925 silver alloy. This formulation can be alloyed from 800 to 935 thousandths.
It offers excellent flowability during casting and is suitable for casting in vacuum systems. During melting, a metal deoxidation process occurs resulting in clean microfusion, leaving minimal slag in the crucible.
925 silver combined with this alloy can be increased in hardness by heat treatment. See the technical table for information on the procedure.
Characteristics:
Composition: Cu 84% In 4% Zn 12%
Grain refinement level: Low
Melting temperature: Solid 795ºC / Liquid 905ºC
Technical data for microfusion
Casting and cylinder temperature for fine pieces (inf. 0.5mm.) · Metal: 980ºC to 1010ºC
· Cylinder: 640ºC to 680ºC
Casting and cylinder temperature for medium pieces (inf. 0.5 to 1.2mm.) · Metal: 960ºC to 980ºC
· Cylinder: 560ºC to 640ºC
Casting and cylinder temperature for parts (over 1.2mm.) · Metal: 940ºC to 960ºC
· Cylinder: 500ºC to 540ºC
Trees Without Stones
Let the crucible cool for 10-15 minutes, then cool in water.
Parameters For Heat Treatment
Temper by solubilization treatment: · Solubilization / 730 ºC / 40 minutes / Immediate cooling with water
· Temper / 300 ºC / 60 minutes / Cooling by air or oven
One-step hardening: · Tempering / 300 ºC / 60 minutes / Cooling by air or oven
It offers excellent flowability during casting and is suitable for casting in vacuum systems. During melting, a metal deoxidation process occurs resulting in clean microfusion, leaving minimal slag in the crucible.
925 silver combined with this alloy can be increased in hardness by heat treatment. See the technical table for information on the procedure.
Characteristics:
Composition: Cu 84% In 4% Zn 12%
Grain refinement level: Low
Melting temperature: Solid 795ºC / Liquid 905ºC
Technical data for microfusion
Casting and cylinder temperature for fine pieces (inf. 0.5mm.) · Metal: 980ºC to 1010ºC
· Cylinder: 640ºC to 680ºC
Casting and cylinder temperature for medium pieces (inf. 0.5 to 1.2mm.) · Metal: 960ºC to 980ºC
· Cylinder: 560ºC to 640ºC
Casting and cylinder temperature for parts (over 1.2mm.) · Metal: 940ºC to 960ºC
· Cylinder: 500ºC to 540ºC
Trees Without Stones
Let the crucible cool for 10-15 minutes, then cool in water.
Parameters For Heat Treatment
Temper by solubilization treatment: · Solubilization / 730 ºC / 40 minutes / Immediate cooling with water
· Temper / 300 ºC / 60 minutes / Cooling by air or oven
One-step hardening: · Tempering / 300 ºC / 60 minutes / Cooling by air or oven